Effect of Electron Beam Irradiation on the Mechanical, Thermal, and Dynamic Mechanical Properties of Flyash and Nanostructured Fly Ash Waste Polyethylene Hybrid Composites

The effect of electron beam irradiation on the technical properties of fly ash (FA) and nano fly ash (NFA)-filled waste polyethylene (WPE) composites have been investigated in this article. It is observed that the FA/NFA at 5 wt% imparted enhanced technical properties. The modified composites were prepared by three different methods (1) modification of WPE matrix first by grafting with maleic anhydride (MA) and preparing the composite (2) Preparing WPE-FA/NFA composites and subjecting to electron beam irradiation. (3) Subjecting the FA/NFA to electron beam radiation first and then preparing composites with WPE. Of the three methods, the composite prepared and then electron beam irradiated gave the best balance in the physico-mechanical properties. The tensile and flexural strength of WPE increased from 21.2 MPa and 25.4 MPa to 33.0 MPa (57.8%) and 45.8 MPa (72%) respectively at 5 wt% FA-filled WPE composites, which further increased to 34.5 MPa (65%) and 47.7 MPa (87.8%) respectively with 5 wt% of NFA-filled WPE composites, after electron beam irradiation. The thermal stability was enhanced upon electron beam irradiation of the composites. The dynamic mechanical properties reveal that the storage modulus reaches the highest value for the irradiated composite corroborating with the flexural modulus throughout the temperature range studied. The fractured surfaces were examined under SEM and were correlated with the mechanical properties. The results indicate that FA/NFA reinforced WPE composites act as an excellent stress raisers preventing crack propagation and enhancing the performance properties on electron beam irradiation. POLYM. COMPOS., 33: 109-119, 2012. (C) 2011 Society of Plastics Engineers