Tailoring of the Perpendicular Magnetization Component in Ferromagnetic Films on a Vicinal Substrate

We have engineered the magnetic properties of 1-8 nm Co films epitaxially grown on an Au-buffered bifacial W(110)/W(540) single crystal. The surface of Au/W(110) was atomically flat, whereas the Au/W(540) followed the morphology of the vicinal W surface, showing a regular array of monoatomic steps. For Co grown on Au/W(540), the existence of the out-of-plane magnetization component extended strongly to a thickness d of about 8 nm, which was accompanied by an anomalous increase of the out-of-plane switching field with increasing d. In addition, the process of up-down magnetization switching could be realized with both a perpendicular and in-plane external magnetic field.