Thick pure palladium film with varied crystal structure electroless deposited from choline chloride-palladium chloride solution without the addition of reductant

Immersion deposition procedure was applied to achieve thick pure palladium films with thickness up to about 3 mu m from choline chloride (ChCl)-palladium chloride (PdCl2) aqueous solution without addition of reductant at 60 degrees C. Using X-ray diffraction and scanning electronmicroscope, it was confirmed that Pd films with different crystal orientations and morphology were obtained just by varying the immersion time, and Pd (111) crystal orientation predominated over other crystal orientations during the initial deposition procedure, while (220) conquered (111) about 45 min later. ChCl performing as a reductant facilitated the growth of thick Pd film free of reductant. The immersion deposition of Pd followed the mechanism of replacement reaction accompanying with autocatalyzed reaction and autocatalyzed reaction predominating over replacement reaction. The results revealed that Pd films prepared from ChCl-PdCl2 solution had excellent properties on solderability and corrosion resistance. (C) 2015 Elsevier B.V. All rights reserved.