Journal
SYNTHETIC METALS
Volume 201, Issue -, Pages 67-75Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.synthmet.2015.01.016
Keywords
Self-assembly; Large area graphene films; Lift-up transfer; p-Doping; XPS
Funding
- European Union [264710]
- Directorate-General for Science, Research and Development of the European Commission
Ask authors/readers for more resources
Solution-processed conductive, flexible and transparent graphene thin films continue drawing attention from science and technology due to their potential for many electrical applications. Here, an up-scalable method for the solution processing of graphite to graphene and further to self-assembled large-area conductive transparent thin-films is presented. The method proceeds via the graphite intercalation route followed by thermal expansion to obtain expanded graphite. The resulting material is dispersed in a surfactant-free mixture of isopropanol and propylene glycol to obtain a stable colloidal dispersion. A graphene thin film is subsequently formed by self-organization at an oil/water interface followed by lift-up transfer to virtually any substrate of interest. Thermally annealed thin-films exhibit a thickness-tunable sheet resistances of between 10 and 0.8 k Omega/square with transparencies between 75% and 45% at 500 nm wavelength, respectively. Additional Au-doping decreases the sheet resistance by a factor of 5. Heating doped films to temperatures above 380 K or exposure to ambient conditions significantly increases the sheet resistance as a result of decreasing charge carrier concentration. The presented method is a simple, up-scalable and thus competitive alternative to other techniques for large area graphene film production. (C) 2015 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available