Type IV Cracking Susceptibility in Weld Joints of Different Grades of Cr-Mo Ferritic Steel

Relative type-IV cracking susceptibility in 2.25Cr-1Mo, 9Cr-1Mo, and 9Cr-1MoVNb ferritic steel weld joint has been assessed. The type-IV cracking was manifested as preferential accumulation of creep deformation and cavitation in the relatively soft intercritical region of heat affected zone of the weld joint. The type-IV cracking susceptibility has been defined as the reduction in creep-rupture strength of weld joint compared to its base metal. The 2.25Cr-1Mo steel exhibited more susceptibility to type-IV cracking at relatively lower temperatures; whereas, at higher temperatures, 9Cr-1MoVNb steel was more susceptible. The relative susceptibility to type-IV cracking in the weld joint of the Cr-Mo steels has been rationalized on the basis of creep-strengthening mechanisms operating in the steels and their venerability to change on intercritical heating during weld thermal cycle, subsequent postweld heat treatment, and creep exposure.