Journal
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
Volume 539, Issue -, Pages 230-237Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2012.01.087
Keywords
Age hardening; Magnesium alloys; Mechanical characterisation; Strength; Ductility
Categories
Funding
- Japan Society for the Promotion of Science (JSPS)
Ask authors/readers for more resources
We report on a quantitative investigation into the effect of size and distribution of rod-shaped 13; precipitates on strength and ductility of a Mg-Zn alloy. Despite precipitation strengthening being crucial for the practical application of magnesium alloys this study represents the first systematic examination of the effect of controlled deformation on the precipitate size distribution and the resulting strength and ductility of a magnesium alloy. Pre-ageing deformation was used to obtain various distributions of rod-shaped beta'(1) precipitates through heterogeneous nucleation. Alloys were extruded to obtain a texture so as to avoid formation of twins and thus to ensure that dislocations were the primary nucleation site. Pre-ageing strain refined precipitate length and diameter, with average length reduced from 440 nm to 60 nm and diameter from 14 nm to 9 nm. Interparticle spacings were measured from micrographs and indicated some inhomogeneity in the precipitate distribution. The yield stress of the alloy increased from 273 MPa to 309 MPa. The yield stress increased linearly as a function of reciprocal interparticle spacing, but at a lower rate than predicted for Orowan strengthening. Pre-ageing deformation also resulted in a significant loss of ductility (from 17% to 6% elongation). Both true strain at failure and uniform elongation showed a linear relationship with particle spacing, in agreement with models for the accumulation of dislocations around non-deforming obstacles. Samples subjected to 3% pre-ageing deformation showed a substantially increased ageing response compared to non-deformed material; however, additional deformation (to 5% strain) resulted in only modest changes in precipitate distribution and mechanical properties. (C) 2012 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available