Journal
MATERIALS & DESIGN
Volume 57, Issue -, Pages 250-257Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.matdes.2014.01.008
Keywords
Equal channel angular pressing; Microstructure; Age hardening treatment; Strength; Microhardness
Categories
Ask authors/readers for more resources
In order to examine the combined effect of plastic deformation and aging process, the Al 7075 alloy was subjected to equal channel angular pressing (ECAP) deformation by route BC in various ECAP and aging conditions: pre-ECAP aging, post-ECAP aging and dynamic aging during ECAP at 393 K and 423 K. Followed by ECAP and aging treatment, Vickers microhardness and tensile test were performed and microstructural observations were undertaken using transmission electron microscopy (TEM) and X-ray diffractometer (XRD). TEM investigation showed that ultrafine-grained (UFG) materials with grain size less than 500 nm could be obtained after three or four passes of ECAP. Precipitates characterization revealed that maximum mechanical properties are achieved when the microstructure mainly consists of fine dispersion of small eta' precipitates and minor quantities of GP zones. Dynamic aged specimens at 393 K and 423 K represented maximum and minimum mechanical properties, respectively, due to formation of fine eta' precipitates plus GP zones and eta' plus eta precipitates, respectively. Dynamic aging during ECAP at 393 K appeared preferable to other procedures for attaining maximum mechanical properties as well as saving time and energy. (C) 2014 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available