Extensional stress-strair measurements on a polyurea (PU) were carried out at strain rates up to 830 s(-1). in combination with expost faceo small-angle X-ray scattering (SAXS) measurements and temperature-dependent SAXS. The elastomer is of interest because of its application as an impact-resistant coating. The highest strain rates used herein fall within the softening, or transition, zone of the viscoelastic spectrum and are thus relevant to the working hypothesis that the performance of a polyurea impact coating is related to its transition to the glassy state when strained very rapidly. While quasi-static and slow deformation of the PU gives rise to irrecoverable strain and anisotropic SAXS patterns. when stretched at high rates the PU recovers completely and the scattering is isotropic. Thus, the deformation of the hard domains observed at low rates is absent at high strain rates. Linear dynamic mechanical measurements were also carried Out. with the obtained segmental relaxation times in good agreement With dielectric relaxation measurements on this material. The PU exhibits the usual breakdown of time-temperature superposition in the transition zone. This thermorheological complexity underlies the fact that published time-temperature shift factors for this material are unrelated to the segmental dynamics, and therefore use of these shift factors to predict the onset of glassy dynamics during impact loading of the PU Will be in error.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available