The precipitation behavior of V(C, N) in steels microalloyed with vanadium was researched using a thermal simulator during single-pass deformation at 800-750 V. The V(C, N) precipitates and its nucleation effect on ferrite were investigated by TEM and EDS. The experimental results show that there are two remarkable heterogeneous nucleation effects of V(C, N) particles precipitated before gamma--> alpha phase change: primary reason is that high coherency between V(C, N) and ferrite promotes V(C, N) to become a nucleating center of intragranular ferrite; secondary reason is that the coarsening of V(C, N) causes locally solute-poor region in austenite, thus expedites the nucleation of intragranular ferrites further. Furthermore, the relationship between the size and shape of V(C, N) was studied, and identification method was provided for distinguishing interphase precipitation and general precipitation to avoid erroneous judgment and misguide.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available