Thermal Failure of Nanostructured Thermal Barrier Coatings with Cold-Sprayed Nanostructured NiCrAlY Bond Coat

Nanostructured thermal barrier coatings (TBCs) were deposited by plasma spraying using agglomerated nanostructured YSZ powder on Inconel 738 substrate with cold-sprayed nanostructured NiCrAlY powder as bond coat. The isothermal oxidation and thermal cycling tests were applied to examine failure modes of plasma-sprayed nanostructured TBCs. For comparison, the TBC consisting of conventional microstructure YSZ and conventional NiCrAlY bond coat was also deposited and subjected to the thermal shock test. The results showed that nanostructured YSZ coating contained two kinds of microstructures; nanosized zirconia particles embedded in the matrix and microcolumnar grain structures of zirconia similar to those of conventional YSZ. Although, after thermal cyclic test, a continuous, uniform thermally grown oxide (TGO) was formed, cracks were observed at the interface between TGO/BC or TGO/YSZ after thermal cyclic test. However, the failure of nanostructured and conventional TBCs mainly occurred through spalling of YSZ. Compared with conventional TBCs, nanostructured TBCs exhibited better thermal shock resistance.