JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS
Volume 2, Issue 6, Pages 607-612Publisher
ELSEVIER
DOI: 10.1016/j.jmbbm.2009.04.003
Keywords
-
Ask authors/readers for more resources
The shear strength of the interface between tiles of aragonite in the nacre of red abalone Haliotis rufescens was investigated through mechanical tensile and shear tests. Dog-bone shaped samples were used to determine the tensile strength of nacre when loaded parallel to the plane of growth; the mean strength was 65 MPa. Shear tests were conducted on a special fixture with a shear gap of 200 mu m, approximately 100 mu m narrower than the spacing between mesolayers. The shear strength is found to be 36.9 +/- 15.8 MPa with an average maximum shear strain of 0.3. Assuming the majority of failure occurs through tile pull-out and not through tile fracture, the tensile strength can be converted into a shear strength of 50.9 MPa. Three mechanisms of failure at the tile interfaces are discussed: fracture of mineral bridges, toughening due to friction created through nanoasperities, and toughening due to organic glue. An additional mechanism is fracture through individual tiles. (C) 2009 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available