POLYMER-PLASTICS TECHNOLOGY AND ENGINEERING
Volume 54, Issue 8, Pages 771-778Publisher
TAYLOR & FRANCIS INC
DOI: 10.1080/03602559.2014.979497
Keywords
Core-shell emulsion polymerization; Polyhedral oligomeric silsesquioxane; Polyacrylate latex; Nanocomposite; Thermal analysis
Categories
Ask authors/readers for more resources
Core-shell nanocomposites were prepared from acrylates, fluorine- containing methacrylate monomers and methylacryloypropyl polyhedral oligomeric silsesquioxanes (MAP-POSS) by emulsion polymerization. The properties of latex and nanocomposites were characterized by FTIR, NMR, TEM, laser particle diameter analyzer, DMA and TGA. The results showed that the particle diameter of composite latexes was about 33.5nm, dynamic mechanical loss peak temperature T-p of the nanocomposites had the best high value at 99.6 degrees C when 7wt.% MAP-POSS was added, which is 7.8 degrees C higher than the pure polyacrylates. MAP-POSS could increase the thermal stability of materials, the initial thermal decomposition temperature increases about 34 degrees C.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available