Starting from a commercial slurry of high purity alpha-Al2O3, freeze-dried powders, cast, filter-pressed or cold isostatically pressed samples were produced. Resulting powders or green bodies showing different particles packing were densified by spark plasma sintering (SPS) to obtain transparent polycrystalline alpha-Al2O3. Microstructure and real in-line transmittance (RIT) after SPS were dependent on the particles packing quality. Avoiding large agglomerates, narrowing the pore size distribution, reducing the most-frequent pore size (D-mode) and avoiding macroscopic heterogeneities within the green bodies enabled high RIT values to be achieved in the visible and near-infrared spectrum. However, a limit was achieved in the preparation of green bodies for which reducing the D-mode had no more influence on the optical behaviour of samples sintered by SPS. Finally, pure alpha-Al2O3 samples presenting a high RIT640nm value of 53% were produced from all the green bodies obtained by the following techniques: filter-pressing, slip casting and cold isostatic pressing. (C) 2012 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available