c-axis oriented ZnO formed in a rotating magnetic field with various rotation speeds

A rotating magnetic field was used to fabricate c-axis oriented zinc oxide. The influence of rotating speed on orientation structure was also examined. The aligned axes had the largest diamagnetic susceptibility, which axis was difficult to align with a static magnetic field. In c-axis oriented ZnO, the degree of orientation (Lotgering factor) in the green compact ranged from 0.2 to 0.5 along c-axis. The Lotgering factor increased with rotating speed. For all samples with the rotating magnetic field, the degrees of orientation increased up to above 0.9 after sintering at 1573 K. (c) 2008 Elsevier Ltd. All rights reserved.