Contact De-electrification of Electrostatically Charged Polymers

The contact electrification of insulating organic polymers is still incompletely understood, in part because multiple fundamental mechanisms may contribute to the movement of charge. This study describes a mechanism previously unreported in the context of contact electrification: that is, contact de-electrification, a process in which polymers charged to the same polarity discharge on contact. Both positively charged polymeric beads, e.g., polyamide 6/6 (Nylon) and polyoxymethylene (Delrin), and negatively charged polymeric beads, e.g., polytetrafluoroethylene (Teflon) and polyamide-imide (Torlon), discharge when the like-charged beads are brought into contact. The beads (both with charges of similar to +/- 20 mu C/m(2), or similar to 100 charges/mu m(2)) discharge on contact regardless of whether they are made of the same material, or of different materials. Discharge is rapid: discharge of flat slabs of like-charged Nylon and Teflon pieces is completed on a single contact (similar to 3 s). The charge lost from the polymers during contact de-electrification transfers onto molecules of gas in the atmosphere. When like-charged polymers are brought into contact, the increase in electric field at the point of contact exceeds the dielectric breakdown strength of the atmosphere and ionizes molecules of the gas; this ionization thus leads to discharge of the polymers. The detection (using a Faraday cup) of charges transferred to the cup by the ionized gas is compatible with the mechanism. Contact de-electrification occurs for different polymers and in atmospheres with different values of dielectric breakdown strength (helium, argon, oxygen, carbon dioxide, nitrogen, and sulfur hexafluoride): the mechanism thus appears to be general.