In this study, digital image correlation was used for two widely different cases to assess the potential and the limitations of the technique for applications at high temperatures. Specifically, digital image correlation was employed in high-temperature low-cycle fatigue experiments in a nickel-based superalloy and in phase transformation experiments conducted on bainitic steel in order to shed light on the microstructural processes. Depending on the type of experiments, the microstructure was characterized prior to the experiments (fatigue) or after the experiments (phase transformation). In the fatigue experiments, it was found that the features dominating damage evolution were the dendrites resulting from the solidification of the cast material. In the phase transformation experiments, variant selection is active when stresses are superimposed during the phase transformation process, which resulted in the evolution of transformation plasticity strains. Thereby, mainly the bainite variants oriented along the [101], [201] and [121] directions were observed to grow parallel to the loading axis, which in turn led to transformation plasticity strains. For validation of the digital image correlation data, average strains were calculated for the surface area probed and compared to strain values obtained by conventional extensometry. In all cases studied, the correlation was satisfactory, indicating that digital image correlation can provide for additional insight into processes active at the micro level.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available