JOURNAL OF POWER SOURCES
Volume 240, Issue -, Pages 676-682Publisher
ELSEVIER
DOI: 10.1016/j.jpowsour.2013.05.014
Keywords
Ionic liquid; Li battery; Li salt; Temperature; Electrolyte
Funding
- National Science Council of Taiwan [NSC 101-ET-E-008-001-ET]
Ask authors/readers for more resources
Lithium hexafluorophosphate (LiPF6) and lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) are used as Li salts in butylmethylpyrrolidinium-bis(trifluoromethanesulfonyl)imide (BMP-TFSI) ionic liquid (IL) electrolyte for Li/LiFePO4 cells. This kind of IL electrolyte shows high thermal stability (>400 degrees C) and non-flammability, and is thus ideal for high-safety applications. At 25 degrees C, a maximum capacity of 113 mAh g(-1) (at 0.1 C) is found for LiFePO4 in the IL with 0.5 M LiTESI. An excessive LiTESI concentration leads to a capacity decrease due to reduced electrolyte ionic conductivity. At 50 degrees C, the measured capacity and rate capability are significantly improved compared to those at 25 degrees C. With 1 M LiTESI-doped IL electrolyte (the optimum concentration,at 50 degrees C), a capacity of 140 mAh g(-1) is found at 0.1 C and 45% of the capacity can be retained when the rate increases to 5 C, values which are comparable to those found in a traditional organic electrolyte. In the IL electrolyte, the LiFePO4 electrode shows better cyclic stability at 50 degrees C than it does at 25 degrees C; this trend is opposite to that found in the organic electrolyte. At 50 degrees C, there is negligible capacity loss of LiFePO4 after 100 charge-discharge cycles in 1 M LiTESI-doped BMP-TFSI IL electrolyte. (C) 2013 Elsevier B.V. All rights reserved(.)
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available