Journal
JOURNAL OF POLYMER RESEARCH
Volume 19, Issue 6, Pages -Publisher
SPRINGER
DOI: 10.1007/s10965-012-9870-0
Keywords
Poly(lactic acid) (PLA); Morphology; Dynamic mechanical thermal analysis (DMTA); Tensile properties; Shape recovery
Categories
Funding
- center of excellence in textiles (CENMIT)
Ask authors/readers for more resources
Physical, thermomechanical, and shape memory properties of two different samples of poly(lactic acid) (PLA) multifilament yarns were determined using various complementary techniques. The birefringence and crystalline fraction of one sample was higher than the other filaments sample indicating higher molecular orientation and compactness. For both filaments, two distinct morphological features with different sizes in the order of few nanometers (less than 50 nm) were found using AFM and SAXS techniques. The glass transition temperature (T-g) of the samples were ranged from 61 degrees C to 76 degrees C depends on the sample and the methods of measurement. Partial storage modulus (E') increase above T(g)as well as additional small peak in loss modulus (E.) of the lower crystallinity sample was assigned to recrystallization. The multiple overlapped peaks in the E. and tan delta curves and subsequent crystallization along with exothermic peak right after T-g suggests the existence of both relaxed and oriented amorphous regions. The rigid crystalline regions prevented the shrinkage and enhanced dimensional stability. Multifilament yarn with higher crystallinity and total molecular orientation showed higher modulus (both dynamic and static) and strength and lower elongation at break. The oriented non-crystalline regions in the multifilament yarn sample led to moderate modulus and strength along with high elongation at break. The shape recovery of both samples with different structural parameters stayed almost constant (similar to 50%) upon the deformation temperature rise.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available