Journal
JOURNAL OF NUCLEAR MATERIALS
Volume 439, Issue 1-3, Pages 41-50Publisher
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jnucmat.2013.03.073
Keywords
-
Funding
- Institute for Plasma Research, Bhat, Gandhinagar
Ask authors/readers for more resources
Effects of tungsten and tantalum contents on impact, tensile, low cycle fatigue and creep properties of Reduced Activation Ferritic-Martensitic (RAFM) steel were studied to develop India-specific RAFM steel. Four heats of the steel have been melted with tungsten and tantalum contents in the ranges 1-2 wt.% and 0.06-0.14 wt.% respectively. Increase in tungsten content increased the ductile-to-brittle transition temperature (DBTT), low cycle fatigue and creep strength of the steel, whereas the tensile strength was not changed significantly. Increase in tantalum content increased the DBTT and low cycle fatigue strength of the steel whereas the tensile and creep strength decreased. Detailed TEM investigations revealed enhanced microstructural stability of the steel against creep exposure on tungsten addition. The RAFM steel having 1.4 wt.% tungsten with 0.06 wt.% tantalum was found to possess optimum combination of impact, tensile, low cycle fatigue and creep properties and is considered for Indian-specific RAFM steel. (C) 2013 Published by Elsevier B.V.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available