Journal
JOURNAL OF NON-CRYSTALLINE SOLIDS
Volume 388, Issue -, Pages 55-61Publisher
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jnoncrysol.2013.12.007
Keywords
Lead free; Bi2O3-B2O3-SiO2 glasses; Front side; IR and Raman spectroscopy; XPS
Funding
- The National Natural Science Fund of China [51205085]
- Cooperation of Industry, Education and Academy Funding from the Education Department of Guangdong province, China [2011B090400238]
Ask authors/readers for more resources
The Bi-based lead-free frit for silicon solar cell front contact has a shortage of conversion efficiency compared with traditional products that contain Pb. One feasible method to increase conversion efficiency is by improving the current flow at the interface. The current flow establishment is controlled by the reaction of Bi ions to Ag. SiNx, and the Si wafer. However, the microstructure of Bi ions in the glasses remains unclear. In this work, two groups of Bi2O3-B2O3-SiO2 glasses were studied through differential scanning calorimetry (DSC), X-ray diffraction (XRD), infrared, and Raman and X-ray photoelectron spectroscopies. The results suggest that the Bi3+ to Bi5+ transformation is induced by the increase in B2O3 content in both the 30 mol% and 60 mol% Bi glasses. The coexistence of [BiO3] and [BiO6] is confirmed in all ternary samples. The [BO4] units exhibit in all borosilicate glass. The [BO3] structure only emerges in a high boron concentration. The glass transition temperature (T-g) is strongly affected by the ratio of Non-Bridging Oxygen. The Oxygen packing density also has influence on Tg but not obvious. (C) 2013 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available