Journal
PHILOSOPHICAL MAGAZINE
Volume 95, Issue 15, Pages 1696-1716Publisher
TAYLOR & FRANCIS LTD
DOI: 10.1080/14786435.2015.1043969
Keywords
corrosion; Ringer's solution; NiTi thin film; XPS; magnetron sputtering
Ask authors/readers for more resources
Thin nanocrystalline amorphous NiTi film was deposited on Si substrate using DC magnetron sputtering. The as-deposited NiTi thin film was crystallized by heat treatment at 500 degrees C for 1h. The crystal structure, surface morphology, microstructure and surface chemistry of the deposited films were studied using X-ray diffraction, atomic force microscopy, scanning electron microscopy and X-ray photoelectron spectroscopy (XPS), respectively. Corrosion behaviour was assessed in Ringer's solution at 37 degrees C by open circuit potential (OCP), potentiodynamic polarization and electrochemical impedance spectroscopy as a function of exposure time. OCP values indicate that the tendency for the formation of a spontaneous oxide film is greater for the NiTi thin films than the bulk NiTi. Long time exposure to Ringer's solution was found to have a great effect on the corrosion behaviour of the samples. Significantly low corrosion current density was obtained for the annealed NiTi film from the potentiodynamic polarization curves indicating a typical passive behaviour, but as-deposited film and bulk NiTi alloy exhibited breakdown of passivity at potentials approximately +1.4V (vs. SCE). XPS showed that the oxide film formed on the annealed NiTi thin film mainly composed of Ti oxides, and no evidence of Ni was found up to 8.2nm beneath the top surface, suggesting the excellent corrosion resistance of this sample in Ringer's solution.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available