Journal
JOURNAL OF MINING AND METALLURGY SECTION B-METALLURGY
Volume 49, Issue 1, Pages 65-70Publisher
TECHNICAL FACULTY, BOR-SERBIA
DOI: 10.2298/JMMB120927025K
Keywords
Nanoparticles; Copper; Silver; Filler; Metal-metal bonding
Categories
Funding
- Hitachi Ltd.
Ask authors/readers for more resources
The present paper describes a metal-metal bonding technique using Cu nanoparticles containing Ag nanoparticles (Ag/Cu nanoparticles). The Ag/Cu nanoparticles with particle sizes of 30-85 nm and crystal sizes of 9.3 nm for Cu and 8.1 nm for Ag were produced by reducing 5.0x10(-3) M Ag+ (AgClO4) and 5.0x10(-3) M Cu2+ (Cu(NO3)(2)) simultaneously with 1.0 M hydrazine in aqueous solution containing 1.0 g/L poly(vinylpyrrolidone) as dispersing agent and 5x10(-3) M citric acid as stabilizer at room temperature. Discs of metallic Cu or metallic Ag were successfully bonded under annealing at 400 degrees C and pressurizing at 1.2 MPa for 5 min in H-2 gas with help of the Ag/Cu particles. The shear strengths required for separating the bonded discs were as large as 19.7 for the Cu discs and 16.0 MPa for the Ag discs
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available