In this study, biodegradation and biocompatibility of novel poly(epsilon-caparolactone)/nano fluoridated hydroxyapatite (PCL-FHA) scaffolds were investigated. The FHA nanopowders were prepared via mechanical alloying method and had a chemical composition of Ca-10 (PO4)(6)OH2-x F (x) (where x values were selected equal to 0.5 and 2.0). In order to fabricate PCL-FHA scaffolds, 10, 20, 30 and 40 wt% of the FHA were added to the PCL. The PCL-FHA scaffolds were produced by the solvent casting/particulate leaching using sodium chloride particles (with diameters of 300-500 mu m) as the porogen. The phase structure, microstructure and morphology of the scaffolds were evaluated using X-ray diffraction, Fourier transform infrared spectroscopy and scanning electron microscopy techniques. Porosity of the scaffolds was measured using the Archimedes' Principle. In vitro degradation of PCL-FHA scaffolds was studied by incubating the samples in phosphate buffered saline at 37A degrees C and pH 7.4 for 30 days. Moreover, biocompatibility was evaluated by MTT assay after seeding and culture of osteoblast-like cells on the scaffolds. Results showed that the osteoblast-like cells attached to and proliferated on PCL-FHA and increasing the porosity of the scaffolds increased the cell viability. Also, degradation rate of scaffolds were increased with increasing the fluorine content in scaffolds composition.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available