The release of nickel from nickel-titanium (NiTi) is strongly reduced by a sub-micrometer thin layer of calcium phosphate deposited by rf-magnetron sputtering

Thin calcium phosphate coatings were deposited on NiTi substrates (plates) by rf-magnetron sputtering. The release of nickel upon immersion in water or in saline solution (0.9% NaCl in water) was measured by atomic absorption spectroscopy (AAS) for 42 days. The coating was analyzed before and after immersion by X-ray powder diffraction (XRD), scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX). After an initial burst during the first 7 days that was observed for all samples, the rate of nickel release decreased 0.4-0.5 ng cm(-2) d(-1) for a 0.5 mu m-thick calcium phosphate coating (deposited at 290 W). This was much less than the release from uncoated NiTi (3.4-4.4 ng cm(-2) d(-1)). Notably, the nickel release rate was not significantly different in pure water and in aqueous saline solution.