JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
Volume 26, Issue 6, Pages 481-486Publisher
JOURNAL MATER SCI TECHNOL
DOI: 10.1016/S1005-0302(10)60077-1
Keywords
TiZr-base alloy; Bulk metallic glass (BMG); Fracture strength
Funding
- Ministry of Science and Technology of China [2006CB605201]
- National Natural Science Foundation of China [50825402]
Ask authors/readers for more resources
Low-cost TiZr-base bulk metallic glasses (BMGs) (Ti36.1Zr33.2Ni5.8Be24.9)(100-x)Cu-x (x=5, 7 and 9) with a maximum size of over 50 mm in diameter were developed by optimizing the alloy composition. The idea is initiated by selecting a particular microstructure comprising primary beta-Ti dendrite and amorphous phase. Afterwards, based on this composition of amorphous phase, a class of TiZr-base bulk metallic glasses was designed step by step to reach the optimum composition range. The glass transition temperature (T-g), initial crystallization temperature (T-x) and width of supercooled region (Delta T) of (Ti36.1Zr33.2Ni5.8Be24.9)(91)Cu-9 BMG are 611, 655 and 44 K, respectively. The (Ti36.1Zr33.2Ni5.8Be24.9)(91)Cu-9 BMG exhibits low density of 5.541 g.cm(-3) and high compressive fracture strength of 1800 MPa, which promises the potential application as structural materials.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available