Nanofibre fabrication in a temperature and humidity controlled environment for improved fibre consistency

Journal

JOURNAL OF MATERIALS SCIENCE
Volume 46, Issue 11, Pages 3890-3898

Publisher

SPRINGER
DOI: 10.1007/s10853-011-5310-5

Keywords

-

Funding

  1. Engineering and Physical Sciences Research Council (EPSRC) under the Innovative Manufacturing Research initiative
  2. EPSRC [EP/E001599/1] Funding Source: UKRI
  3. Engineering and Physical Sciences Research Council [EP/E001599/1] Funding Source: researchfish

Ask authors/readers for more resources

Fabricating nanofibres with reproducible characteristics is an important demand in the membrane industry in order to establish commercial viability. In this study, the effect of controlled atmospheric conditions on electrospun cellulose acetate (CA) nanofibres was evaluated for temperatures ranging 17.5-32.5 A degrees C and relative humidity ranging 20-70%. CA solution (0.2 g/mL) in a solvent mixture of acetone/dimethylformamide/ethanol (2:2:1) was electrospun into nonwoven fibre mesh with the fibre diameter ranging from 150 nm to 1 mu m. The resulting nanofibres were analysed by differential scanning calorimetry, showing a correlation of reducing melt enthalpy with increasing atmospheric temperature. The opposite was seen with increasing atmospheric humidity, which conferred increasing melt enthalpy. Analysis of scanning electron microscopy images provided a correlation of reducing average fibre diameter with increasing atmospheric temperature and increasing fibre diameter with increasing atmospheric humidity. These results correlate with the melt enthalpy results, suggesting that finer CA nanofibres infer a lower melt enthalpy. Together these studies provide strong evidence that the controlled atmospheric conditions affect the fibre diameter of the resulting electrospun nanofibres. A salient observation in this study was that increased humidity reduced the effect of fibre beading yielding a more consistent and therefore better quality of fibre. This has apparent implications for the reproducibility of nanofibre production and offers a new method of controlling fibre morphology. This study has highlighted the requirement to control atmospheric conditions during the electrospinning process to fabricate reproducible fibre mats.

Authors

I am an author on this paper
Click your name to claim this paper and add it to your profile.

Reviews

Primary Rating

4.6
Not enough ratings

Secondary Ratings

Novelty
-
Significance
-
Scientific rigor
-
Rate this paper

Recommended

No Data Available
No Data Available