The nanostructured SnO(2)@C spheres with tin oxide cores and carbon shells were prepared by a facile one-pot solvothermal method followed by a subsequent calcination at 600 C in a high-purity nitrogen atmosphere. The resulting samples were characterized with thermogravimetric analysis (TGA), X-ray diffraction (XRD), energy-dispersive spectroscopy (EDS), infrared spectroscopy (IR), X-ray photoelectron spectroscopy (XPS), field-emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), and charge-discharge test. Electrochemical performance test showed that these SnO(2)@C core-shell spheres exhibited an initial discharge specific capacity of 667.4 mAh/g in the potential range of 1.2-0.01 V. After 18 cycles, the capacity of the SnO(2)@C core-shell spheres anode stabilized reversibly at about 370 mAh/g. This improved cycling performance could be attributed to the carbon shells, which can enhance the conductivity of SnO(2) and suppress the aggregation of active particles to increase their structure stability during cycling. These SnO(2)@C core-shell spheres are promising anodes for lithium ion batteries. This study provides a facile way to improve the cycle ability of transition oxides for reversible lithium-ion storage.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available