Journal
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY
Volume 210, Issue 10, Pages 1411-1418Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jmatprotec.2010.04.002
Keywords
Instability; Keyhole; Melting front; Laser welding; Porosity; Fiber laser; Crack repair; Heat-treatable aluminum alloy
Funding
- NSF [CMMI-0738044]
- Department of MAE, NC State University
Ask authors/readers for more resources
The causes of instability are investigated for low speed welding of aluminum from 10 mm/s down to 1 mm/s using a 300 W single-mode fiber laser Results show that the welding is stable until the speed drops below a certain threshold (similar to 1 mm/s) at which there was a significant change in the process mechanism. causing shallow, inefficient welds with many defects A power distribution model and several tests are used to examine different types of power losses at low speeds It is then hypothesized that, at low speeds. the CW laser beam mainly irradiates at the molten pool, which absorbs a large portion of the beam energy near the surface The majority of this absorbed energy subsequently is either lost via evaporation or transferred into the bulk material via convection and conduction without being used for melting the solid at the welding front. A laser pulsing scheme was used to test the above hypothesis It was found that, through proper control of the duty cycle and frequency to prevent overheating of the molten pool, a high aspect ratio weld shape can be restored at low speeds, thus, confirming the hypothesis. In addition, the 1 mm/s low speed threshold is found to be related to the initial molten pool propagation speed, which is found to be approximately 14 mm/s. Although this paper does not propose a solution to restore process stability, the understanding of the instability origin will be helpful in the search of such a solution to overcome the process instability for slow speed welding of aluminum (C) 2010 Elsevier B V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available