Single-layer graphene nanosheets with controlled grafting of polymer chains

Single-layer graphene nanosheets (SLGNs) are prepared by reduction of well-exfoliated graphite oxide aided by a surfactant (sodium dodecylbenzene sulfonate, SDBS). Grafting density and polystyrene (PS) chain lengths are controlled by modulating the concentrations of diazonium compound and monomer during the grafting reaction of the initiator and the succeeding atomic transfer radical polymerization (ATRP). Atomic force microscopy (AFM), X-ray diffraction (XRD), Raman spectra and transmission electron microscopy (TEM) are used to confirm the single-layer structure of graphene sheets, covalent bonding at the interface, and distribution uniformity of grafting PS chains at the SLGN surface. Thermogravimetric analysis (TGA) is performed to assess the control of grafting density and chain length. PS chains grafted on the SLGN surface exhibited remarkably confined relaxation behavior. An increase in the glass transition temperature (T-g) of up to 18 degrees C is observed for high grafting density, low molecular weight polymer-grafted graphene samples. The low grafting density, high molecular weight sample shows an increase in T-g of similar to 9 degrees C, which is attributed to superior heat conduction efficiency. The measured thermal conductivity for the PS composite film with 2.0 wt% SLGNs increase by a factor of 2.6 compared to that of the pure PS.