Journal
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
Volume 349, Issue -, Pages 35-44Publisher
ELSEVIER
DOI: 10.1016/j.jmmm.2013.08.043
Keywords
Magnetic nanoparticle; Graphitic carbon; Iron oxide nanoparticle; Iron nanoparticle
Funding
- Minerva Grant
Ask authors/readers for more resources
Magnetic iron oxide (Fe3O4 and gamma-Fe2O3) and iron carbide (Fe3C) nanoparticles of different geometrical shapes: cubes, spheres, rods and plates, have been prepared by thermal decomposition of a mixture containing the metal precursor Fe(CO)(5) and the stabilizer polyvinylpyrrolidone (PVP) at 300 degrees C in a sealed cell under inert atmosphere. The thermal decomposition process was performed for 4 or 24 h at ([PVP]/[Fe(CO)(5)]) (w/v) ratio of 1:1 or 1:5. Elemental iron nanospheres embedded within a mixture of amorphous and graphitic carbon coating were obtained by hydrogen reduction of the prepared iron oxide and iron carbide nanoparticles at 450 degrees C. The formation of the graphitic carbon phase at such a low temperature is unique and probably obtained by catalysis of the elemental iron nanoparticles. Changing the annealing time period and the ([PVP]/[Fe(CO)(5)]) ratio allowed control of the composition, size, size distribution, crystallinity, geometrical shape and magnetic properties of the different magnetic nanoparticles. (C) 2013 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available