Luminescence induced by elastic deformation of ZnS:Mn nanoparticles

When the thin film of ZnS:Mn nanoparticles deposited on a glass substrate is elastically deformed by applying a load, then initially the mechanoluminescence (ML) intensity increases with time, attains a peak value I-m at a particular time t(m), and later on it decreases with time. The rise and decay characteristics of the ML produced during release of the load are also similar to those produced during the application of load. Similar rise, occurrence of peak and then decrease in ML intensity are also found, when the film is deformed impulsively by dropping a steel ball of small mass from a low height; however, in this case, the time durations for the occurrence of ML and decay time of ML are very short. In the cases of loading and impulsive deformation after t(m), initially the ML intensity decreases at a fast rate and then at a slow rate, in which the decay time of fast decrease is equal to the time-constant for rise of pressure and the decay time for slow decrease is equal to the relaxation time of the surface charges. In the case of loading, the peak intensity I-m, and the total intensity I-T of ML increase quadratically with the magnitude of applied pressure; however, in the case of impulsive deformation, both the I-m and I-T increase linearly with the height through which the ball is dropped on to the sample. In the case of deformation of the samples at a fixed strain rate, I-m should increase linearly with the applied pressure. The elastico ML in ZnS:Mn nanoparticles can be understood on the basis of the piezoelectrically-induced electron detrapping model, in which the local piezoelectric field near the Mn2+ centres reduces the trap-depth, and therefore, the detrapping of filled electron traps takes place, and subsequently the energy released non-radiatively during the electron-hole recombination excites the Mn2+ centres and de-excitation gives rise to the ML The equal number of photons emitted during the application of pressure, release of pressure, and during the successive applications of pressure, indicates that the detrapped electron-traps get filled during the relaxation of the surface charges induced by the application and release of pressure because the charge carriers move to reduce the surface charges. On the basis of the piezoelectrically-induced electron detrapping model, expressions are derived for different characteristics of the ML of ZnS:Mn nanoparticles and a good agreement is found between the theoretical and experimental results. The expressions explored for the dependence of ML intensity on several parameters may be useful in tailoring the suitable nanomaterials capable of exhibiting ML during their elastic deformation. The values of the relaxation time of surface charges, time-constant for the rise of pressure, and the threshold pressure can be determined from the measurement of the time-dependence of ML. It seems that the trapping and detrapping of charge carriers in materials can be studied using ML. (C) 2009 Elsevier B.V. All rights reserved.