JOURNAL OF ELECTRONIC MATERIALS
Volume 39, Issue 2, Pages 230-237Publisher
SPRINGER
DOI: 10.1007/s11664-009-0992-z
Keywords
Soldering; Cu-Zn; under bump metallurgy (UBM)
Categories
Funding
- National Science Council, Taiwan [NSC-97-2221-E-007-021-MY3]
Ask authors/readers for more resources
Zn additions to Cu under bump metallurgy (UBM) in solder joints were the subject of this study. An alternative design was implemented to fabricate pure Sn as the solder and Cu-xZn (x = 15 wt.% and 30 wt.%) as the UBM to form the reaction couple. As the Zn content increased from 15 wt.% to 30 wt.% in the Sn/Cu-Zn system, growth of both Cu3Sn and Cu6Sn5 was suppressed. In addition, no Kirkendall voids were observed at the interface in either Sn/Cu-Zn couple during heat treatment. After 40-day aging, different multilayered phases of [Cu6Sn5/Cu3Sn/Cu(Zn)] and [Cu6Sn5/Cu(Zn,Sn)/CuZn] formed at the interface of [Sn/Cu-15Zn] and [Sn/Cu-30Zn] couples, respectively. The growth mechanism of intermetallic compounds (IMCs) during aging is discussed on the basis of the composition variation in the joint assembly with the aid of electron-microscopic characterization and the Sn-Cu-Zn ternary phase diagram. According to these analyses of interfacial morphology and IMC formation in the Sn/Cu-Zn system, Cu-Zn is a potential UBM for retarding Cu pad consumption in solder joints.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available