Influence of steaming on the acidity and the methanol conversion reaction of HZSM-5 zeolite

The influence of steaming at varying temperatures on the physicochemical properties of a HZSM-5 zeolite (Si/Al = 27) was investigated by X-ray diffraction, Al-27 MAS NMR, Ar physisorption and IR spectroscopy of adsorbed pyridine, 2,4,6-trimethylpyridine and CO. The catalytic activity of the zeolites was evaluated in propane and methanol conversion reactions. Mild steaming did not result in removal of framework Al atoms. Instead, evidence was found that some extra-framework Al atoms present in the parent zeolite were inserted into the framework at defect sites. This resulted in higher propane conversion rates. Severe steaming resulted in a strong decrease in the framework Al content and agglomeration of extra-framework Al atoms. This caused a strong decrease in the Bronsted acidity probed by pyridine and CO IR. The rate of propane conversion was consequently adversely affected. The steaming procedures did not result in the formation of noticeable mesoporosity. By IR spectroscopy of adsorbed 2,4,6-trimethylpyridine, however, indications were found for structural damage at the outer region of the zeolite crystals, resulting in increased accessibility of the Bronsted acid sites (BAS). For methanol conversion at 350 degrees C, the concentration of BAS governs the catalytic performance. For zeolites with a high BAS density (parent and mildly steamed zeolites), the rate of deactivation is high. The total amount of methanol converted per BAS is relatively low because of the high rate of consecutive reactions. These reactions involve the conversion of the dehydration product of methanol, dimethyl ether, to products with carbon-carbon bonds and the formation of carbonaceous deposits, which deactivate the zeolite catalyst. Decreasing Bronsted acidity by severe steaming results in an increased amount of methanol converted per BAS because of the lower coke formation rate. As a result, the total amount of methanol converted per BAS increases strongly with decreasing BAS density. However, it also causes lower rates of conversion of dimethyl ether to useful products. In terms of the total amount of methanol converted per BAS to light olefins, the set of zeolites shows optimum performance at intermediate BAS density (HZSM-5 severely steamed at 450 degrees C; concentration of BAS similar to 0.2 mmol g(-1)). (C) 2013 Elsevier Inc. All rights reserved.