Synthesis and Properties of Novel Fluorinated Epoxy Resins

Journal

JOURNAL OF APPLIED POLYMER SCIENCE
Volume 120, Issue 1, Pages 148-155

Publisher

WILEY
DOI: 10.1002/app.32911

Keywords

fluorinated epoxy resins; dielectric properties; thermal stability

Ask authors/readers for more resources

A novel fluorinated epoxy compound, 4,4'-bis(2,3-epoxypropoxy-phenyl)-1-(3-trifluoromethylphenyl)-2,2,2-trifluoroethane (BEF), was synthesized starting from the coupling of phenol with 3'-trifluoromethyl-2,2,2-trifluroacetophenone catalyzed by Lewis acid to yield an intermediate compound, which was then converted to the fluorinated epoxy by epoxidation with epichlorohydrin. BEF could be thermally cured with organic anhydride or aromatic amine as curing agents to produce thermally cured epoxy resins. Experimental results demonstrated that the thermally cured fluorinated epoxy resins showed good thermal stability with decomposition temperature at 5% weight loss of 342-364 degrees C in nitrogen, high glass transition temperature (T-g) of 165-171 degrees C (determined by DMA), and outstanding mechanical properties with flexural strengths of 79-119 MPa, flexural moduli of 2085-2130 MPa. The thermally cured fluorinated epoxy resins also exhibited excellent electric insulating properties with volume resistivity of 1.59-9.23 10(16) Omega cm and surface resistivity of 4.81 x 10(15)-7.70 x 10(16) Omega. The dielectric constants at 1 MHz were measured in the range of 3.1-3.4 and the dielectric dissipation factor (tan delta) in the range of 1.38-2.48 x 10(-3). It was found that the fluorinated epoxy resins have improved electric insulating and dielectric properties as well as lower moisture adsorption compared with the corresponding commercial Bisphenol A type epoxy resins. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 120: 148-155, 2011

Authors

I am an author on this paper
Click your name to claim this paper and add it to your profile.

Reviews

Primary Rating

4.6
Not enough ratings

Secondary Ratings

Novelty
-
Significance
-
Scientific rigor
-
Rate this paper

Recommended

No Data Available
No Data Available