The mechanism of the effect of n-GaN thickness on the internal quantum efficiency (IQE) in InxGa1-xN multiple-quantum-wells (MQWs) grown on GaN/Si by means of metal organic chemical vapor deposition has been investigated by x-ray diffractometry, photoluminescence, and transmission electron microscopy. It is found that the increasing n-GaN thickness obviously improves the IQE in InxGa1-xN MQWs. It is clarified that the threading dislocation density (TDD) directly determines the V-defect density and the V-defect density is lower than the TDD. As the n-GaN thickness increases from 1.0 to 2.0 mu m, the TDD significantly decreases by one order of magnitude. The V-defect density obviously reduces from 3.9 x 10(9) cm(-2) to 8.7 x 10(8) cm(-2), while the IQE in InxGa1-xN MQWs is improved from 28.3 to 44.6%. As the GaN thickness increases, the V-defect density in the InxGa1-xN MQW decreases due to the reduction of TDD in GaN, and subsequently the nonradiative recombination centers are effectively eliminated due to the reduction of the V-defect density in the InxGa1-xN MQWs. (C) 2011 American Institute of Physics. [doi: 10.1063/1.3596592]
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available