We have newly synthesized the alpha-Mn structured Mn3Ge thin films on GaAs(001) substrate. The single phase Mn3Ge film was grown at a growth temperature of 150 degrees C, while the secondary phase was observed above a growth temperature of 250 degrees C. The Mn3Ge films exhibited ferrimagnetism with a Curie temperature of 334 K. The saturation magnetizations were 255.9 and 313.8 emu/cm(3) and the corresponding coercive fields were 453 and 1166 Oe at 10 K for the samples grown at 150 and 300 degrees C, respectively. The ferrimagnetism was confirmed by the anomalous Hall effect data. (C) 2011 American Institute of Physics. [doi:10.1063/1.3543777]
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available