Highly efficient removal of arsenic metal ions with high superficial area hollow magnetite nanoparticles synthetized by AACVD method

New nanotechnology alternatives and methodologies have been developed in order to overcome the limitations of conventional techniques for metal ions removal from water. Currently, the removal of heavy metals requires multiple steps which include the separation and post-treatment of the generated sludge. Usually, this sludge is composed of dangerous environmental pollutants mixed with the material used for removing the metal ion. Thus, the removal of these metals becomes a challenging task. Herein we report the synthesis of magnetite nanoparticles with high specific area by the aerosol assisted chemical vapour deposition method. Deposition temperature were fixed at 450 degrees C and a mixture of Ar-air were used as a carrier gas, a flow of 1.0 and 0.015 L min (1) were used for Ar and air, respectively. The precursor solution was a dilution of Fe (II) chloride in methanol, with different concentration 0.01, 0.05 and 0.1 mol dm (3). The crystalline structure of the nanoparticles was characterized by grazing incidence X-ray diffraction. Morphology and microstructure were analyzed by field emission scanning electron microscopy, scanning probe microscopy and transmission electron microscopy. Magnetic properties were evaluated with a vibrating sample magnetometer and specific area was measured by the Brunauer-Emmett-Teller method. To determine the removal efficiency of arsenic ion from water, several tests were carried out at six exposition times 1, 3, 5, 10, 20 and 30 min. Results showed high removal efficiency, more than 99%, in less than 1 min. (C) 2012 Elsevier B. V. All rights reserved.