Aluminum alloy; Precipitation; Erbium; Zirconium
Categories
Funding
- National Key Basic Research & Development Plan Project [2012CB619503]
- National Natural Science Foundation [51201003, 51101001]
- Beijing Municipal Science Foundation of Education Commission [KM201310005002]
Ask authors/readers for more resources
The temporal evolution of the Al-3(ErZr) precipitates is investigated in Al-0.04Er-0.04Zr and Al-0.04 Er-0.08Zr alloys during aging at elevated temperature of 450 and 500 degrees C. The results show that the coarsening behavior of the precipitates in both alloys is similar, due to the core-shell structure with Zr segregated in the shell of the Al-3(ErZr) precipitates. With the increase of the amount of Zr addition, the misfit between the precipitate and the Al matrix decreases, consequently the coherency transition size of the precipitates in Al-0.04Er-0.08Zr is larger than that of Al-0.04Er-0.04Zr. After aging at 500 degrees C for 100 h, some of the precipitates in Al-0.04Er-0.08Zr transform to D0(23) structure due to the high Zr/Er ratio, while the precipitates in Al-0.04Er-0.04Zr keep the L1(2) structure. (C) 2013 Published by Elsevier B.V.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available