JOURNAL OF ALLOYS AND COMPOUNDS
Volume 574, Issue -, Pages 377-382Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2013.05.134
Keywords
Lithium ion battery; Cathode material; LiNi0.8Co0.15Al0.05O2; LiNi1/3Co1/3Mn1/3O2; Coating
Ask authors/readers for more resources
Electrochemically active material, LiNi1/3Co1/3Mn1/3O2, was chosen to coat LiNi0.8Co0.15Al0.05O2 particle by a co-precipitation method with a weight ratio of 3: 97. The thickness of coating layer is about 300 nm observed clearly by cross-section SEM photos. The coated material showed better electrochemical performance than that of the un-coated sample. At room temperature, the initial discharge capacity of the coated material was 188.2 mA h g(-1) at 0.2C between 2.8 and 4.3 V and retained 96.2% after 100 cycles. Moreover, the discharge capacities of the coated cathode material at 50 degrees C could retain 163.2 mA h g(-1) after 100 cycles. The composite also had a good rate performance with a capacity of about 146.3 mA h g(-1) at 2C rate. Electrochemical impedance spectroscopy measurements showed that the coated material had a lower charge-transfer resistance. (C) 2013 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available