JOURNAL OF ALLOYS AND COMPOUNDS
Volume 564, Issue -, Pages 130-137Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2013.02.157
Keywords
Mg-Li alloy; Sn addition; Extrusion; Microstructure; Mechanical property
Categories
Funding
- Technology R&D Program for Energy [20112010300030]
- Ministry of Knowledge Economy (MKE, Korea)
Ask authors/readers for more resources
this work, Mg-3 wt%Zn-1 wt%Sn-0.4 wt%Mn alloys with different Li addition (5, 8 and 11 wt%) were melted and extruded at 200 degrees C. Effects of Li addition on microstructure and mechanical properties of ascast and as-extruded Mg-xLi-3Zn-1Sn-0.4Mn alloys were investigated. Li addition to Mg-3Zn-1Sn0.4Mn based alloy resulted in the formation of MgLi2Sn intermetallic compound. By Li addition from 5 wt% to 8 and 11 wt%, the ductility was significantly increased from 18.1% to 30.9% and 49.3% at room temperature due to transformation from HCP to BCC crystal structure and formation of a weaker basal texture of the alpha-Mg phase region. The ultimate tensile strength (UTS) was decreased from 252.0, 201.1 and 148.7 MPa as Li content increased from 5 to 8 and 11 wt%. On the other hand, the tensile strength of Sn containing alloys was remarkably increased compared to the alloys without Sn addition due to the presence of the fine MgLi2Sn intermetallic compounds. (C) 2013 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available