High-throughput analysis for preparation, processing and analysis of TiO2 coatings on steel by chemical solution deposition

A high-throughput preparation, processing and analysis of titania coatings prepared by chemical solution deposition from water-based precursors at low temperature (approximate to 250 degrees C) on two different types of steel substrates (Aluzinc (R) and bright annealed) is presented. The use of the high-throughput equipment allows fast preparation of multiple samples saving time, energy and material; and helps to test the scalability of the process. The process itself includes the use of IR curing for aqueous ceramic precursors and possibilities of using UV irradiation before the final sintering step. The IR curing method permits a much faster curing step compared to normal high temperature treatments in traditional convection devices (i.e., tube furnaces). The formulations, also prepared by high-throughput equipment, are found to be stable in the operational pH range of the substrates (6.5-8.5). Titanium alkoxides itself lack stability in pure water-based environments, but the presence of the different organic complexing agents prevents it from hydrolysis and precipitation reactions. The wetting interaction between the substrates and the various formulations is studied by the determination of the surface free energy of the substrates and the polar and dispersive components of the surface tension of the solutions. The mild temperature program used for preparation of the coatings however does not lead to the formation of pure crystalline material, necessary for the desired photocatalytic and super-hydrophilic behavior of these coatings. Nevertheless, some activity can be reported for these amorphous coatings by monitoring the discoloration of methylene blue in water under UV irradiation. (c) 2012 Elsevier B.V. All rights reserved.