Al-Mg-Si alloys; Primary Mg2Si; Refinement; Modification; Al-P master alloy
Categories
Funding
- National Science Fund for Distinguished Young Scholars [50625101]
- Key Project of Science and Technology Research of Ministry of Education of China [106103]
Ask authors/readers for more resources
Refinement and modification performance of Al-3P master alloy on primary Mg2Si in Al-12.67Mg-10.33Si alloys were investigated in this paper. The experimental results show that the perfect effect can be obtained after the addition of 3% Al-3P master alloy into the Al-Mg-Si alloys. The morphologies of primary Mg2Si particulates change from dendritic to polygonal shape, and their average sizes decrease from similar to 100 to similar to 20 mu m. Further, the ultimate tensile strength increases from 252 to 275 MPa. Also, the melt treating technological parameters were established in this paper, treating temperature is 850 degrees C, holding time is 30 min. EPMA results show that All particles act as the nuclei of primary Mg2Si. (C) 2007 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available