Volume 18, Issue 6, Pages 599-606Publisher
SPRINGER HEIDELBERG
DOI: 10.1007/s11581-011-0653-0
Keywords
Cellulose acetate; Dielectric permittivity; Electrical modulus; Loss tangent
Funding
- Universiti Teknologi MARA (NSF)
Ask authors/readers for more resources
The present work deals with the findings on the dielectric behaviour of cellulose acetate (CA) and its complexes consisting of ammonium tetrafluoroborate (NH4BF4) and polyethylene glycol with a molecular weight of 600 g/mol (PEG(600)) that were prepared using the solution casting method. The highest sigma obtained for CA-NH4BF4 film was 2.18 x 10(-7) S cm(-1) and enhanced to 1.41 x 10(-5) S cm(-1) with the addition of 30 wt.% PEG(600). The dielectric behaviours of the selected samples were analyzed using complex impedance Z*, complex admittance A*, complex permittivity E >*, and complex electric modulus M*-based frequency and temperature dependence in the range of 10 Hz-1 MHz and 303-363 K, respectively. The variation in dielectric permittivity (epsilon (r) and epsilon (i)) as a function of frequency at different temperatures exhibits a dispersive behaviour at low frequencies and decays at higher frequencies. The variation in dielectric permittivity as a function of temperature at different frequencies is typical of polar dielectrics in which the orientation of dipoles is facilitated with the rising temperature, and thereby the permittivity is increased. Modulus analysis was also performed to understand the mechanism of electrical transport process, whereas relaxation time was determined from the variation in loss tangent with temperature at different frequencies.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available