Journal
INTERNATIONAL JOURNAL OF MATERIALS RESEARCH
Volume 105, Issue 12, Pages 1236-1238Publisher
CARL HANSER VERLAG
DOI: 10.3139/146.111137
Keywords
Microwave sintering; Porous ceramics; Dielectric properties; Silicon nitride
Categories
Funding
- National Science Foundation of China [51272090, 51372099]
- Doctoral Found of Jinan University [XBS1310]
- Program for Scientific research innovation team in Colleges and Universities of Shandong Province
Ask authors/readers for more resources
Porous silicon nitride ceramics were fabricated without pore formers via microwave sintering. Microwave sintering at different temperatures produced unique microstructures with high porosity. The best porous silicon nitride ceramics were fabricated at 1 550 degrees C for 30 min; the resulting product had a bulk density of 1 552 g cm(-3), an open porosity of 43.9 %, and a flexural strength of 43.6 MPa. The mean pore channel size and the dielectric constants of the fabricated porous silicon nitride ceramics ranged from 0.1 mu m to 1 mu m and 2.9 to 3.4 under different temperatures, respectively.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available