MICROPOROUS AND MESOPOROUS MATERIALS
Volume 204, Issue -, Pages 99-105Publisher
ELSEVIER
DOI: 10.1016/j.micromeso.2014.10.050
Keywords
Metal organic framework; Membranes; Synthesis; Permeation; Stability
Categories
Funding
- National Science Foundation [CBET-1160084]
- Directorate For Engineering
- Div Of Chem, Bioeng, Env, & Transp Sys [1160084] Funding Source: National Science Foundation
Ask authors/readers for more resources
Large pore zeolitic imidazolate framework (ZIF) membranes offer potential for separation of gases with different adsorption affinity on ZIF crystals and separation of liquid molecules by molecular sieving. In this work continuous, highly crystalline, largely c-oriented ZIF-68 membranes were reproducibly synthesized on macroporous zinc oxide supports by the reactive seeding method. The membranes were roughly 50 microns thick and the single component gas permeance measurements obtained adhered to Knudsen diffusion, indicating the presence of limited nonselective defects. The membranes were found to be highly stable at room temperature and ambient conditions, although immersion in water at room temperature and 100 degrees C caused irreparable damage to the ZIF-68 crystallinity. Immersion in organic solvents did not render the crystallinity notably altered. A prolonged p-xylene pervaporation run indicated that ZIF-68 membranes were susceptible to fouling, by showing an approximately 55% decrease in p-xylene pervaporation flux from when the membrane was fresh to the second data point tested at 4 h. The extent of fouling equilibrated after 4 h on-stream and the pervaporation flux remained constant throughout the remainder of testing. The membrane crystallinity was not degraded by p-xylene pervaporation. (C) 2014 Elsevier Inc. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available