Thermal stability study of SDC/Na2CO3 nanocomposite electrolyte for low-temperature SOFCs

The novel core-shell nanostructured SDC/Na2CO3 composite has been demonstrated as a promising electrolyte material for low-temperature SOFCs. However, as a nanostructured material, stability might be doubted under elevated temperature due to their high surface energy. So in order to study the thermal stability of SDC/Na2CO3 nanocomposite, XRD, BET, SEM and TGA characterizations were carried on after annealing samples at various temperatures. Crystallite sizes, BET surface areas, and SEM results indicated that the SDC/Na2CO3 nanocomposite possesses better thermal stability on nanostructure than pure SDC till 700 degrees C. TGA analysis verified that Na2CO3 phase exists steadily in the SDC/Na2CO3 composite. The performance and durability of SOFCs based on SDC/Na2CO3 electrolyte were also investigated. The cell delivered a maximum power density of 0.78 W cm(-2) at 550 degrees C and a steady output of about 0.62 W cm(-2) over 12 h operation. The high performances together with notable thermal stability make the SDC/Na2CO3 nanocomposite as a potential electrolyte material for long-term SOFCs that operate at 500-600 degrees C. (C) 2009 Professor T. Nejat Veziroglu. Published by Elsevier Ltd. All rights reserved.