Micro-arc oxidation; Ceramic coating; Aluminium 6061 alloy; Infrared emissivity; Pulsed bipolar current mode
Categories
Ask authors/readers for more resources
MAO ceramic coatings were prepared on aluminium 6061 surfaces at different treating durations (10, 20, ... 60 min), using alkali silicate electrolyte and pulsed bipolar current mode. The surface microstructures and properties were studied using SEM, XRD, EDX and a surface roughness tester. Image-Pro Plus and MATCH! softwares were used to analyze SEM micrographs and XRD results, respectively. The infrared emissivities of the ceramic coatings were measured at the 70 degrees C using FTIR spectrometer. We found a linear correlation between the volcano-like area and the surface roughness. The compositions and phases were associated with the volcano-like population and area. The curve of IR spectral emissivity was influenced by surface roughness, gamma-alumina, sillimanite and cristobalite phases. The emissivity was enhanced by the surface roughness in the ranges 4.0-9.6 mu m and 10.5-14.8 mu m. In the range 7.0-8.0 mu m, alpha-alumina and sillimanite phases enhanced the emissivity, while the cristobalite has a negative impact to the emissivity. A negative contributions were found for alpha-alumina in the region 9.6-16.0 mu m and for the surface thickness in the region 15.0-16.0 mu m. Overall, the average of long wave infrared (LWIR) emissivity ranged from 87.05% to 91.65%. (C) 2013 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available