Journal
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
Volume 628, Issue -, Pages 188-197Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2015.01.031
Keywords
Additive manufacturing; Selective laser melting; Aluminium; Cellular lattice structures; Compression behaviour; 3D quantification
Categories
Funding
- Seventh European Frame Programme (FP 7) [NMP-SE-2012-0313781]
- Engineering and Physical Science Research Council, UK [EP/I02249X/1, EP/F028431/1]
- Engineering and Physical Sciences Research Council [EP/F028431/1, EP/I02249X/1, EP/J021229/1] Funding Source: researchfish
- EPSRC [EP/I02249X/1, EP/F028431/1, EP/J021229/1] Funding Source: UKRI
Ask authors/readers for more resources
AlSi10Mg cellular lattice structures have been fabricated by selective laser melting (SLM) using a range of laser scanning speeds and powers. The as-fabricated strut size, morphology and internal porosity were investigated using optical microscopy (OM), scanning electron microscopy (SEM) and X-ray microtomography (micro-CT) and correlated to the compressive properties of the structure. Strut diameter was found to increase monotonically with laser power while the porosity was largest at intermediate powers. Laser scanning speed was found to thicken the struts only at slow rates while the porosity was largest at intermediate speeds. High speed imaging showed the melt pool to be larger at high laser powers. Further the melt pool shape was found to vary cyclically over time, steadily growing before becoming increasingly instable and irregularly shaped before abruptly falling in size due to splashing of molten materials and the process repeating. Upon compressive loading, lattice deformation was homogeneous prior to the peak stress before falling sharply due to the creation of a (one strut wide) shear band at around 45 to the compression axis. The specific yield strength expressed as the yield stress/(yield stress of the aluminium x relative density) is not independent of processing conditions, suggesting that further improvements in properties can be achieved by process optimisation. Lattice struts failed near nodes by a mixture of ductile and brittle fracture. (C) 2015 Elsevier B.V. All rights reserved.