Journal
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
Volume 636, Issue -, Pages 10-23Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2015.02.031
Keywords
Zirconium; Twinning; Neutron diffraction; Two-phase materials
Categories
Funding
- NSERC
- UNENE
- Nu-Tech Precision Metals under the Industrial Research Chair program in Nuclear Materials at Queen's University
Ask authors/readers for more resources
A series of in situ compression tests have been carried out at room temperature on three dual-phase Zr-2.5 wt% Nb alloys with different concentrations of the interstitial alloying elements oxygen and iron. Oxygen and iron are potent strengthening additives in two-phase alloys with a hexagonal-close packed alpha phase and body-centred cubic beta phase, such as the Zr-Nb and Ti-V-Al systems. The evolution of interphase stress, along with the progression of twinning, were monitored during deformation by neutron diffraction. The twin volume fraction measured following deformation was not strongly dependent on ingot chemistry, contrary to previously reported results. Annealing in the alpha+beta and the beta region allowed for variation in the initial residual stress distribution and crystallographic texture, respectively, and the effect of these parameters on deformation mode selection was also investigated. Interstitial oxygen has a greater strengthening effect on prismatic < a > slip than on basal < a > slip at room temperature. High impurity contents were not observed to suppress {10 (1) over bar2}< 10 (1) over bar1 > tensile twinning. Despite being an alpha-stabilizer, oxygen is observed to strengthen the beta phase under suitable heat treatment conditions. (C) 2015 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available